Chemical Composition | Mechinical Properties | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Specification | Grade | C % Max | Mn % Max | P % Max | S % Max | CE Max | Nb +Ti+V% | Yield Strength Mpa Min | Ultimate Tensile Strength Min Mpa | Elongation % in Gauge Length 5.65 √S | Charpy Impact Value Jpules Min | Bend Test Min | ||
<20 mm | 20-40 mm | >40 mm | ||||||||||||
IS 2062/1999 | A | 0.230 | 1.5 | 0.050 | 0.050 | 0.42 | - | 250 | 240 | 230 | 410 | 23 | 3T | |
B | 0.220 | 1.5 | 0.045 | 0.045 | 0.41 | - | 250 | 240 | 230 | 410 | 23 | 27 | 2T/3T* | |
For IS 2062/ 1999 Si 0.40% max. | ||||||||||||||
*2T for £25 mm thickness. 3T for > 25 mm thickness |
Size in MM | Thickness in MM | ||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|
ISA | 3 | 4 | 5 | 6 | 8 | 10 | 12 | 15 | 16 | 18 | 20 |
20 x 20 | 0.900 | 1.100 | |||||||||
25 x 25 | 1.100 | 1.400 | 1.800 | ||||||||
30 x 30 | 1.400 | 1.800 | 2.200 | ||||||||
35 x 35 | 1.600 | 2.100 | 2.600 | 3.000 | |||||||
40 x 40 | 1.800 | 2.400 | 3.000 | 3.500 | |||||||
45 x 45 | 2.100 | 2.700 | 3.400 | 4.000 | |||||||
50 x 50 | 2.300 | 3.000 | 3.800 | 4.500 | |||||||
55 x 55 | 4.100 | 4.900 | 6.400 | 7.900 | |||||||
60 x 60 | 4.500 | 5.400 | 7.000 | 8.600 | |||||||
65 x 65 | 4.900 | 5.800 | 7.700 | 9.400 | |||||||
70 x 70 | 5.300 | 6.300 | 8.300 | 10.200 | 11.000 | ||||||
75 x 75 | 5.700 | 6.800 | 8.900 | 11.000 | |||||||
80 x 80 | 7.300 | 9.600 | 11.800 | 14.000 | |||||||
90 x 90 | 8.200 | 10.800 | 13.400 | 15.800 | |||||||
100 x 100 | 9.200 | 12.100 | 14.900 | 17.700 | |||||||
110 x 110 | 13.400 | 16.500 | 19.600 | 24.200 | |||||||
130 x 130 | 15.900 | 19.700 | 23.400 | 28.900 | |||||||
150 x 150 | 22.800 | 27.200 | 33.600 | 35.800 | 39.900 | 44.100 | |||||
200 x 200 | 36.600 | 45.400 | 48.500 | 54.000 | 60.000 |