Chemical Composition | Mechinical Properties | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Specification | Grade | C % Max | Mn % Max | P % Max | S % Max | CE Max | Nb +Ti+V% | Yield Strength Mpa Min | Ultimate Tensile Strength Min Mpa | Elongation % in Gauge Length 5.65 √So | Charpy Impact Value Jpules Min | Bend Test Min | ||
<20 mm | 20-40 mm | >40 mm | ||||||||||||
IS 2062/1999 | A | 0.230 | 1.5 | 0.050 | 0.050 | 0.42 | - | 250 | 240 | 230 | 410 | 23 | 3T | |
B | 0.220 | 1.5 | 0.045 | 0.045 | 0.41 | - | 250 | 240 | 230 | 410 | 23 | 27 | 2T/3T* | |
For IS 2062/ 1999 Si 0.40% max. | ||||||||||||||
*2T for £25 mm thickness. 3T for > 25 mm thickness |
Designation | Size mm x mm | Weight Kg/M | Designation | Size mm x mm | Weight Kg/M |
---|---|---|---|---|---|
M S Beam | H Beam | ||||
100 | 100 x 75 | 11.5 | 150 | 150 x 150 | 27.1 |
125 | 125 x 75 | 13 | 150 | 150 x 150 | 30.6 |
150 | 150 x 80 | 14.9 | 150 | 150 x 150 | 34.3 |
175 | 175 x 90 | 19.3 | 150 | 150 x 150 | 37.1 |
200 | 200 x 100 | 25.4 | 200 | 200 x 200 | 37.3 |
225 | 225 x 110 | 31.2 | 200 | 200 x 200 | 40 |
250 | 250 x 125 | 37.3 | 200 | 200 x 200 | 49.4 |
300 | 300 x 140 | 44.2 | 225 | 225 x 225 | 43.1 |
350 | 350 x 140 | 52.4 | 225 | 225 x 225 | 46.8 |
400 | 400 x 140 | 61.6 | 250 | 250 x 250 | 51 |
450 | 450 x 150 | 72.4 | 250 | 250 x 250 | 54.7 |
500 | 500 x 180 | 86.9 | 300 | 300 x 250 | 58.8 |
550 | 550 x 190 | 103.7 | 300 | 300 x 250 | 63 |
600 | 600 x 210 | 122.6 | 400 | 400 x 250 | 77.4 |
400 | 400 x 250 | 82.2 | |||
450 | 450 x 250 | 87.2 | |||
450 | 450 x 250 | 92.5 |