Chemical Composition | Mechinical Properties | |||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Specification | Grade | C % Max | Mn % Max | P % Max | S % Max | CE Max | Nb +Ti+V% | Yield Strength Mpa Min | Ultimate Tensile Strength Min Mpa | Elongation % in Gauge Length 5.65 √So | Charpy Impact Value Jpules Min | Bend Test Min | ||
<20 mm | 20-40 mm | >40 mm | ||||||||||||
IS 2062/1999 | A | 0.230 | 1.5 | 0.050 | 0.050 | 0.42 | - | 250 | 240 | 230 | 410 | 23 | 3T | |
B | 0.220 | 1.5 | 0.045 | 0.045 | 0.41 | - | 250 | 240 | 230 | 410 | 23 | 27 | 2T/3T* | |
For IS 2062/ 1999 Si 0.40% max. | ||||||||||||||
*2T for £25 mm thickness. 3T for > 25 mm thickness |
Designation | Size mm x mm | Weight Kg/M | Designation | Size mm x mm | Weight Kg/M | Designation | Size mm x mm | Weight Kg/M |
---|---|---|---|---|---|---|---|---|
ISMC | ISMC Light | ISMC Heavy | ||||||
75 | 75 x 40 | 6.8 | 75 | 75 x 40 | 5.7 | 125H | 125 X 66 | 13.7 |
100 | 100 x 50 | 9.2 | 100 | 100 x 50 | 7.9 | 150H | 150 X 76 | 17.7 |
125 | 125 x 65 | 12.8 | 125 | 125 x 65 | 10.7 | 175H | 175 x 76 | 21.7 |
150 | 150 x 75 | 16.4 | 150 | 150 x 75 | 14.4 | 200H | 200 X 76 | 24.3 |
175 | 175 x 75 | 19.2 | 175 | 175 x 75 | 17.6 | 225H | 225 x 83 | 30.7 |
200 | 200 x 75 | 22.2 | 200 | 200 x 75 | 20.6 | 250H | 250 x 82 | 34.2 |
225 | 225 x 80 | 26 | 225 | 225 x 90 | 24 | 250H | 250 X 84 | 38.1 |
250 | 250 x 80 | 30.4 | 250 | 250 x 100 | 28 | 300H | 300 X 92 | 41.5 |
300 | 300 x 90 | 35.9 | 300 | 300 x 100 | 33.1 | 300H | 300 X 94 | 46.2 |
350 | 350 x 110 | 42.2 | 350 | 350 x 100 | 38.9 | |||
400 | 400 x 110 | 49.5 | 400 | 400 x 100 | 45.8 |